Sinteżi tal-mullite

Il-metodu ta 'sinteżi ta' mullite jista 'jinqasam f'metodu ta' sinterizzazzjoni u metodu ta 'tidwib elettriku. Il-metodu tas-sinterizzazzjoni jista 'jinqasam f'metodu niexef u metodu imxarrab skond il-mod ta' preparazzjoni tal-materja prima. Il-proċess niexef huwa li itħan l-ingredjenti flimkien u mbagħad jaħarqu permezz ta 'forn li jdur jew forn tal-mina wara li tagħfas ballun jew kompatt. Il-proċess imxarrab huwa li itħan il-materjal kompost f'demel likwidu bl-ilma, imbagħad agħfas u ffiltra biex jiddeidrat f'kejk tat-tajn, u għafas it-tajn bil-vakwu fis-sezzjoni tat-tajn jew vojt tat-tajn u mbagħad ħruq.
Il-metodu tat-tidwib elettriku huwa li żżid il-materjal kompost mal-forn tal-ark, dewweb fit-temperatura għolja ffurmata mill-ark, kristallizzazzjoni friska, l-użu ta 'ingredjenti naturali ta' materja prima (bħal boksajt, eċċ.) jista 'jiġi mgħaffeġ direttament għal<1.5mm particles without grinding, and then mixed with other powdered raw materials in the mixer.
Is-sinteżi tal-mullite permezz tas-sinterizzazzjoni ġeneralment titwettaq f'1650 ~ 1700 grad. Il-fatturi ewlenin li jaffettwaw is-sinteżi tal-mullite permezz tas-sinterizzazzjoni huma l-purità tal-materja prima, il-finezza tal-materja prima u t-temperatura tal-kalċinazzjoni. Is-sinteżi tal-mullite bil-metodu tas-sinterizzazzjoni tiddependi prinċipalment fuq Al? O? Ir-reazzjoni tal-fażi solida bejn SiO2 u sio2 titlesta, għalhekk it-titjib tat-tixrid tal-materja prima se jaċċellera l-proċess ta 'reazzjoni tal-fażi solida. B'mod partikolari, il-partiċelli<8μm have a great effect on the formation and sintering of synthetic mullite. It can be seen that the full mixing and fine grinding of raw materials is an important process condition to promote the solid phase of the synthesis of mullite. Mullite generally begins to form at 1200 ° C and ends at 1650 ° C. At this time, it is microcrystalline, and the crystallization develops well when the temperature exceeds 1700℃. It can be seen that the combustion temperature directly affects the formation and crystal development of mullite. Therefore, heating to a certain firing temperature and extending a certain holding time are necessary conditions for the synthesis of mullite. The purity of the raw materials used to synthesize mullite is very strict, and a small amount of impurities will reduce the content of mullite. In industrial production, it is inevitable to bring a variety of impurities, mainly Fe? O? TiO? , CaO, MgO, Na? O·K? O, the most harmful of which is Na? O, K? O, they inhibit the formation of mullite and lead to the production of a large number of silicon-rich glass phases, reducing mullite content. Fe? O? It will slow down the mullite process and increase the amount of glass phase. Be TiO? When a small amount of Ti ions exist, part of Ti ions enter the mullite lattice to form a solid solution, promoting the formation of mullite and crystal development and growth, when the TiO2 content is too high, it still acts as a flux.
Il-mullite ta 'l-elettrotidwib jitħejja billi jdub il-kompost f'forn ta' l-ark elettriku, u l-mullite jitkessaħ mit-tidwib. Il-proċess ta 'kristallizzazzjoni huwa simili għal dak ta' Al? O? -SiO? Il-proċess ta 'kristallizzazzjoni tad-dijagramma tal-fażi tas-sistema huwa simili. Meta l-Al? O? Meta l-kompożizzjoni teoretika tal-mullite tkun ogħla minn 71.8%, jiġi ffurmat Al żejjed maħlul. O? Is-soluzzjoni solida tal-mullite, beta-mullite, hija biss Al? O? Il-fażi tal-kurundun tidher biss fi 80%. Il-kompożizzjoni tal-fażi minerali tal-mullite mdewba hija ġeneralment kristall tal-mullite u fażi tal-ħġieġ. L-istandard tal-industrija tal-mullite tad-dewweb elettriku taċ-Ċina YB/T 104-2004 "Mullite mdewba elettrika" il-prodott tal-mullite mdewweb elettriku skond Al? O? Il-kontenut huwa maqsum fi gradi DM-1 u DM-2, u l-kundizzjonijiet tekniċi rilevanti jistgħu jidhru fl-istandards nazzjonali korrispondenti. Meta mqabbel mal-mullite sinterizzat, il-kristalli tal-mullite mdewba huma żviluppati tajjeb bi ħbub kbar u inqas difetti, u d-daqs tal-kristall huwa mijiet ta 'drabi dak tal-mullite sinterizzat, għalhekk il-proprjetajiet mekkaniċi ta' temperatura għolja u r-reżistenza għall-erożjoni huma relattivament tajbin.